Constitutive law of metallurgical phase transformations in solids without mechanical interaction (law called directly by PL8TM in Lagamine).
Prediction of metallurgical phase transformations for a given evolution of the temperature field.
Prepro: LMETA.F
Plane stress state | YES |
Plane strain state | YES |
Axisymmetric state | YES |
3D state | YES |
Generalized plane state | YES |
Line 1 (2I5, 60A1) | |
---|---|
IL | Law number |
ITYPE | 312 |
COMMENT | Any comment (up to 60 characters) that will be reproduced on the output listing. |
Line 1 (6I5) | |
---|---|
NDPO | Maximum degree of polynomials |
NT1 | Maximum number of proeutectoid |
NT2 | Temperatures in the pearlite |
NT3 | Data tables related to bainite |
IJKL | Phase code: = 0 the phase does not exist = 1 the phase can appear I = proeutectoid J = pearlite K = bainite L = martensite |
IMETA | Code defining the order of the material parameters |
Line 1 (2G10.0) | |
---|---|
ALAMB | initial heat conductivity ($\lambda_o$) |
RHOC | initial heat capacity per unit volume ($\rho c_o$) |
These parameters are to be given at the initial temperature and for the initial metallurgical composition of the solid.
5
SIG(1) | current volume fraction of austenite |
SIG(2) | current volume fraction of proeutectoïd |
SIG(3) | current volume fraction of pearlite |
SIG(4) | current volume fraction of bainite |
SIG(5) | current volume fraction of martensite |
6
Q(1) | SCHEIL's sum |
Q(2) | current hardness |
Q(3) | heat generated by phase transformations |
Q(4) | current heat conductivity ($\lambda$); its initial value is $\lambda_o$ |
Q(5) | current heat capacity per unit volume ($\rho_o$); its initial value is $\rho c_o$ |
Q(6) | incubation code = 0 : SCHEIL's sum computed normally = 1 : SCHEIL's sum multiplied by a germination factor (FINCU) |